Título : Preferential orientation of poly (ethylene 2,6-naphthalate) melt-crystallized on the friction-transfer layer of PTFE
Autor : Novillo Logroño, Fernando Augusto
Fujita, Masahiro
Tsuji, Masaki
Kohjiya, Shinzo
Palabras clave : MELT CRISTALIZADO
CAPA DE TRANSFERENCIA DE FRICCIÓN
Fecha de publicación : 1998
Editorial : Tokyo: The Society of Fiber Science and Technology
Citación : Novillo Logroño, Fernando Augusto y otros (1998). Preferential orientation of poly (ethylene 2,6-naphthalate) melt-crystallized on the friction-transfer layer of PTFE. Sen'i Gakkaishi 54: 544-549
Resumen : Solution-cast thin films of poly (ethylene 2, 6-naphthalate) (PEN) were isothermally crystallized at 190°C on the highly oriented ultra-thin friction-transfer layer of polytetrafluoroethylene (PTFE), after being melted at 300°C. Transmission electron microscopy (TEM) of the films showed that PEN crystallized in an oriented fashion on the layer. Selected-area electron diffraction (ED) indicated that the crystals in the PEN films are mostly the α-form, as expected from our thermal condition for crystallization. The ED pattern from the untilted specimen was characterized by the fairly intense arc-shaped 010 reflection on the equator. A series of ED patterns, which were obtained from the same specimen area tilted at various angles around the axis parallel or perpendicular to the chain axis of PTFE in a TEM column, suggested that the crystallites of PEN α-form are preferentially oriented with their chain axis being parallel to the chain axis of PTFE and moreover, with their (100) planes being parallel to the surface of the PTFE layer.
URI : http://www.dspace.uce.edu.ec/handle/25000/14471
Aparece en las colecciones: Artículos Indexados

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Preferential orientation of poly (ethylene 2,6-naphthalate).pdfARTÍCULO A TEXTO COMPLETO2.53 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.