Título : Experimental results of diffusion coefficient of sulfate ions in cement type 10 and class G.
Autor : Cóndor, José
Asghari, Koorosh
Unatrakarn, Datchawan
Palabras clave : CAPTURA Y ALMACENAMIENTO DE DIÓXIDO DE CARBONO
SECUESTRO GEOLÓGICO
DETERIORO DEL CEMENTO
SULFATO
MODELADO DE PERFILES
Fecha de publicación : 2011
Editorial : Ámsterdan: Elsevier
Citación : Cóndor, José y otros (2011). Experimental results of diffusion coefficient of sulfate ions in cement type 10 and class G. Energy Procedia, 4: 5267–5274
Resumen : This paper presents the results of lab experiments done with cement samples in sulfate environment. About 350 samples of cement type 10 and class G were prepared and placed into three temperatures conditions (30, 55, and 75ºC) and three sulfate concentrations (3,000; 6,000; and 30,000 ppmW) for periods of 2, 4, 6, 8, and 10 months. Sulfur concentration (profile) was measured using the scanning electron microscope; SEM. Diffusion coefficient was calculated by matching lab profiles with curves obtained from a Mathlab code created for this purpose. Apart from obtaining the values for diffusion coefficient for sulfate, another main finding was the relationship of sulfate concentration and temperature. At certain threshold temperature, the effects of sulfate diffusion on cement deterioration were more pronounced. The results show that the diffusion coefficient for SO4 was in the order of 3.0 x 10-12 m2 /s to 4.2 x 10-12 m2 /s with small differences in cement type 10 and class G. Also it was noticed that samples exposed at temperature equals to 55ºC, and sulfate concentration equals to 6,000 ppmW had more significant changes when compared to the results obtained from tests conducted at the all other experimental conditions.
URI : http://www.dspace.uce.edu.ec/handle/25000/14792
Aparece en las colecciones: Artículos Indexados

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Experimental results of diffusion coefficient of sulfate ions in cement type 10 and class G.pdfARTÍCULO A TEXTO COMPLETO628.97 kBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.